Compósitos de concreto com adições híbridas de fibras
Carregando...
Tipo
TCC
Data de publicação
2020-12-10
Periódico
Citações (Scopus)
Autores
Mendes, Eder Giovane Nobre
Campos, Larissa Cardia Garmes de
Araujo, Matheus Gonçalves Veludo
Vieira, Matthaus Klinsmann Duarte
Lira, Thomaz Francisco Albuquerque
Campos, Larissa Cardia Garmes de
Araujo, Matheus Gonçalves Veludo
Vieira, Matthaus Klinsmann Duarte
Lira, Thomaz Francisco Albuquerque
Orientador
Pacheco, Caroline Valadão
Título da Revista
ISSN da Revista
Título de Volume
Membros da banca
Programa
Resumo
A fim de observar o comportamento da matriz cimentícia de um concreto reforçado com adição hibrida de fibra, o presente trabalho se utiliza de diferentes teores de adição de fibras, que são aço, polipropileno e aramida, para possibilitar uma ampla gama de análises. O objetivo deste artigo é apresentar os ganhos ou perdas de tenacidade e resistência a compressão do concreto FCK 25MPa relacionadas aos diferentes percentuais de adições de fibras. Para isso, foram moldados corpos de prova com teores diversos das três fibras e então realizado o Ensaio Barcelona Simplificado e o ensaio de resistência a compressão axial. Tendo os resultados dos ensaios, foi possível atestar que as fibras de polipropileno e aramida têm como características auxiliar a resistividade na macrofissuração. Visto que elas possuem alta porosidade, consequentemente tendo alta absorção de água, a elevação dos teores dessas fibras diminui significativamente a trabalhabilidade do concreto. Em contrapartida, as fibras de aço possuem maior módulo de elasticidade e maior auxílio na microfissuração. Além do que os traços que dispõem de maior teor de aço contam com o maior ganho inicial de resistência a compressão.
In order to observe the behavior of the concrete matrix of a reinforced concrete with hybrid addition of fibers, this article uses different ratios of addition of fibers, which are steel, polypropylene and aramid, to enable a wide range of analyzes. The objective of this article is to present the gains or losses of toughness and compressive resistance of FCK 25MPa concrete in relation to the different proportions of fiber additions. For this, specimens with different contents of the three fibers were molded and then put through the Barcelona Simplified Test and the axial compression strength test. Having the data from the tests, it was possible to attest that the polypropylene and aramid fibers have characteristics that resist macrofissure. Since they have high porosity, and consequently high water absorption rates, the increase quantity of these fibers significantly decreases the workability of the concrete. In contrast, steel fibers have greater modulus of elasticity and greater resistance to microfissures. In addition, the specimens that have a higher steel content have the greatest initial gain in compressive resistance.
In order to observe the behavior of the concrete matrix of a reinforced concrete with hybrid addition of fibers, this article uses different ratios of addition of fibers, which are steel, polypropylene and aramid, to enable a wide range of analyzes. The objective of this article is to present the gains or losses of toughness and compressive resistance of FCK 25MPa concrete in relation to the different proportions of fiber additions. For this, specimens with different contents of the three fibers were molded and then put through the Barcelona Simplified Test and the axial compression strength test. Having the data from the tests, it was possible to attest that the polypropylene and aramid fibers have characteristics that resist macrofissure. Since they have high porosity, and consequently high water absorption rates, the increase quantity of these fibers significantly decreases the workability of the concrete. In contrast, steel fibers have greater modulus of elasticity and greater resistance to microfissures. In addition, the specimens that have a higher steel content have the greatest initial gain in compressive resistance.
Descrição
Palavras-chave
concreto , fibras com adição hibrida , compósito , concrete , hybrid addition of fibers , composites