Experimental investigation of delta phase precipitation in inconel 625 superalloy aged at 550, 625 and 725 °C
Tipo
Artigo
Data de publicação
2020
Periódico
Materials Research
Citações (Scopus)
7
Autores
Baldan R.
da Silva A.A.A.P.
Tanno T.M.
da Costa E.T.
Brentegani J.V.N.
Couto A.A.
da Silva A.A.A.P.
Tanno T.M.
da Costa E.T.
Brentegani J.V.N.
Couto A.A.
Orientador
Título da Revista
ISSN da Revista
Título de Volume
Membros da banca
Programa
Resumo
© 2020 Universidade Federal de Sao Carlos. All rights reserved.The δ is an important stable phase that replaces the metastable γ'' in the microstructure of Inconel 625 superalloy. The present work aims to investigate the kinetic of δ-phase precipitation in the microstructure of Inconel 625 nickel-based superalloy aged at 550, 625 and 725 °C up to 1000 h. Aging temperatures were chosen based on the thermodynamic simulation using JMatPro software which indicated that this phase is stable at temperatures below 905 °C. Microstructure of the heat-treated samples was analyzed via SEM/EDS and microhardness evolution was performed by Vickers microhardness tests. The results have shown that the samples aged at 550 °C (all times), 625 °C (all times) and 725 °C up to 200 h did not presented microstructural evidences of δ precipitation. However, samples aged at 725 °C for 500 and 1000 h clearly presented an acicular δ-phase precipitated mainly at the grain boundaries. It was noted changes in the microhardness at different aging time and temperatures probably due to the presence of γ'' and/or δ phases. The sample aged at 625 °C for 1000 h presented the highest microhardness value (333 ± 10 HV).
Descrição
Palavras-chave
Assuntos Scopus
Aging temperatures , Aging time and temperatures , Experimental investigations , Inconel 625 superalloys , Microhardness evolutions , Nickel- based superalloys , Thermodynamic simulations , Vickers microhardness tests