Argamassa com adição de nano magnetita
Carregando...
Tipo
TCC
Data de publicação
2020-12-10
Periódico
Citações (Scopus)
Autores
Bolzoni, Fábio dos Santos
Oliveira, Guilherme Haddad Andraus de
Moya, Lucca Grammenopoulos
Barbieri, Victor Boscardin
Oliveira, Guilherme Haddad Andraus de
Moya, Lucca Grammenopoulos
Barbieri, Victor Boscardin
Orientador
Pacheco, Caroline Valadão
Título da Revista
ISSN da Revista
Título de Volume
Membros da banca
Programa
Resumo
O presente estudo aborda diversos experimentos já realizados envolvendo a adição de Nano Magnetita em materiais cimentícios, analisando as melhorias obtidas nas propriedades mecânicas e físicas com a adição de teores que variaram entre 0,05% e 5%. Além disso, foram feitos experimentos com a adição de 1%, 3% e 5% do nanomaterial em relação ao cimento em corpos de prova de argamassa, analisando as variações na resistência à compressão, nos índices de absorção e de vazios e na velocidade de propagação das ondas por ultrassom, aos 7, 14 e 28 dias de cura dos corpos de prova. Os resultados obtidos apontam a melhora em até 23% na resistência à compressão, uma diminuição de até 10% na absorção de água e no índice de vazios e o aumento da velocidade de propagação das ondas de ultrassom
The present study addresses several experiments already carried out involving the addition of Nano Magnetite in cementitious materials, analysing the improvements obtained in the mechanical and physical properties with the additions of contents that varied between 0,05% and 5%. Besides that, experiments were carried out with the addition of 1%, 3% and 5% of the nanomaterial in relation to cement in mortars specimens, analysing the variations in the compressive strength, in the absorption of water and void ratio and in the speed of the propagation of ultrasound waves, after 7, 14 and 28 days of curing of the specimens. The results obtained shows an improvement of up to 23% in the compressive strength, a decrease of up to 10% in water absorption and void ratio and an increase in the speed of the propagation of ultrasound waves.
The present study addresses several experiments already carried out involving the addition of Nano Magnetite in cementitious materials, analysing the improvements obtained in the mechanical and physical properties with the additions of contents that varied between 0,05% and 5%. Besides that, experiments were carried out with the addition of 1%, 3% and 5% of the nanomaterial in relation to cement in mortars specimens, analysing the variations in the compressive strength, in the absorption of water and void ratio and in the speed of the propagation of ultrasound waves, after 7, 14 and 28 days of curing of the specimens. The results obtained shows an improvement of up to 23% in the compressive strength, a decrease of up to 10% in water absorption and void ratio and an increase in the speed of the propagation of ultrasound waves.
Descrição
Palavras-chave
nano magnetita , argamassa , propriedades mecânicas e físicas , nano magnetite , mortar , mechanical and physical properties