Study of high temperature mechanical behavior of the thermally oxidized Ti-6Al-4V alloy

Página do item simplificado
dc.contributor.authorSeverino B.P.
dc.contributor.authorCouto A.A.
dc.contributor.authorReis D.A.P.
dc.contributor.authorAguiar C.L.
dc.contributor.authorCastagnet M.
dc.contributor.authorMoura Neto C.
dc.date.accessioned2024-03-13T01:02:43Z
dc.date.available2024-03-13T01:02:43Z
dc.date.issued2014
dc.description.abstractThe influence of oxidation of a Ti-6Al-4V alloy at 800 °C on its tensile properties at 600 °C has been studied. Specimens of this alloy were oxidized at 800 °C for 0.5, 1, 5, 10, 20 and 40 h. Tensile tests at 600 °C were carried out and the fracture surfaces were also examined. Oxidation of the specimens resulted in the formation of an oxide layer that spalled and another oxide layer that adhered to the substrate. Oxide formation increased with increase in duration of oxidation. In this investigation, density curves of the oxide layer as a function of duration of oxidation at 800 °C were used to identify a parabolic oxide growth law. The results of this study revealed coherence between the experimental data and calculations based on the Pilling-Bedworth law. The mechanical strength of the Ti-6Al-4V alloy did not vary significantly with oxidation, but reduction in cross sectional area with increase in oxide layer thickness, as well as the slope of the stress-strain curve decreased beyond the ultimate tensile strength. Fracture of the tensile tested specimens was predominantly ductile with microcavities. At certain regions of the oxide layer, brittle fracture with radial cracks was observed indicating intergranular fracture. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
dc.description.firstpage269
dc.description.issuenumber4
dc.description.lastpage280
dc.description.volume45
dc.identifier.doi10.1002/mawe.201400226
dc.identifier.issn1521-4052
dc.identifier.urihttps://dspace.mackenzie.br/handle/10899/36506
dc.relation.ispartofMaterialwissenschaft und Werkstofftechnik
dc.rightsAcesso Restrito
dc.subject.otherlanguagehigh temperatures
dc.subject.otherlanguageOxidation
dc.subject.otherlanguageTi-6Al-4V
dc.titleStudy of high temperature mechanical behavior of the thermally oxidized Ti-6Al-4V alloy
dc.typeArtigo
local.scopus.citations5
local.scopus.eid2-s2.0-84898464653
local.scopus.subjectCross sectional area
local.scopus.subjectHigh temperature
local.scopus.subjectHigh temperature mechanical behavior
local.scopus.subjectIntergranular fracture
local.scopus.subjectOxide layer thickness
local.scopus.subjectThermally oxidized
local.scopus.subjectTi-6al-4v
local.scopus.subjectUltimate tensile strength
local.scopus.updated2024-05-01
local.scopus.urlhttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84898464653&origin=inward
Arquivos
Coleções
Artigos de periódico